Added with bio-rare earth components to deliver excellent fluorescence and opalescence effects.
Manufactured with large-scale 99% platinum production equipment using biological-grade 99.9% pure natural mineral raw materials. The ceramic blocks are pure, free of impurities and discoloration spots.
Physical, chemical and aesthetic properties comparable to European products.
Excellent casting fluidity and good compatibility with investment materials from various brands.
| Parameter | Value |
| Three-point flexural strength after crystallization | 420MPa ± 60MPa |
| Density after crystallization | 2.46 ~ 2.52g/cm³ |
| Coefficient of thermal expansion (CTE 50-500) after crystallization | 10.5×10K¹ |
| Linear shrinkage rate | 0.0010-0.0026 (≈0.2%) |
| Vickers hardness HV1 | 6500MPa ± 200MPa |
| Elastic modulus | 50 ± 10GPa |
| Fracture toughness | 2.8-3.8MPa·m¹/² |
| Chemical solubility after crystallization | < 100μg/cm² |
| Cytotoxicity after crystallization | Grade 0 |
Indications：Crown restorations,Inlays,Veneers
Dental Heat-Pressed Glass Ceramic Blocks
| Translucency\Color | A1 | A2 | A3 | A3.5 | A4 | B1 | B2 | B3 | B4 | C1 | C2 | C3 | C4 | D1 | D2 | D3 | D4 | 0M1 | 0M2 | 0M3 | 0M3+(BL4) |
| HT | √√ | √ | √ | √√ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ |
| MT | √ | ||||||||||||||||||||
| LT | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ | √ |